| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.15 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）2(230°C/3.8kg) |
|
ASTMD1238 |
5.0 |
g/10min |
| 物理性能 |
收缩率-流动(注塑) |
|
ASTMD955 |
0.50to0.70 |
% |
| 机械性能 |
抗张强度3(屈服,注塑) |
|
ASTMD638 |
41.4 |
MPa |
| 机械性能 |
TensileStrength4(Break,23°C,3.18mm,InjectionMolded) |
|
ASTMD638 |
33.8 |
MPa |
| 机械性能 |
TensileElongation4(Yield,23°C,3.18mm,InjectionMolded) |
|
ASTMD638 |
2.3 |
% |
| 机械性能 |
TensileElongation4(Break,23°C,3.18mm,InjectionMolded) |
|
ASTMD638 |
9.6 |
% |
| 机械性能 |
FlexuralModulus-Tangent5(InjectionMolded) |
|
ASTMD790A |
2340 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm) |
|
ASTMD256A |
140 |
J/m |
| 硬度 |
洛氏硬度(R级) |
|
ASTMD785 |
98 |
|
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,3.18mm,InjectionMolded) |
|
ASTMD648A |
71.1 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,退火,3.18mm) |
|
ASTMD648 |
92.2 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15256 |
93.3 |
°C |
| 热性能 |
RTIElec(1.5mm) |
|
UL746 |
60.0 |
°C |
| 热性能 |
RTIImp(1.5mm) |
|
UL746 |
60.0 |
°C |
| 热性能 |
RTIStr(1.5mm) |
|
UL746 |
60.0 |
°C |
| 可燃性 |
UL阻燃等级(1.5mm,ALL) |
|
UL94 |
V-0 |
|