| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
6.5 |
g/10min |
| 薄膜 |
割线模量-MD |
|
ASTMD882 |
168 |
MPa |
| 薄膜 |
SecantModulus-TD |
|
ASTMD882 |
199 |
MPa |
| 薄膜 |
抗张强度-MD(屈服) |
|
ASTMD882 |
9.20 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield) |
|
ASTMD882 |
9.23 |
MPa |
| 薄膜 |
抗张强度-MD(断裂) |
|
ASTMD882 |
20.8 |
MPa |
| 薄膜 |
抗张强度-TD(断裂) |
|
ASTMD882 |
18.2 |
MPa |
| 薄膜 |
伸长率-MD(断裂) |
|
ASTMD882 |
390 |
% |
| 薄膜 |
TensileElongation-TD(Break) |
|
ASTMD882 |
680 |
% |
| 薄膜 |
落锤冲击 |
|
ASTMD1709A |
76 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
|
ASTMD1922 |
440 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
|
ASTMD1922 |
200 |
g |
| 光学性能 |
光泽度(45°) |
|
ASTMD2457 |
82 |
|
| 光学性能 |
雾度 |
|
ASTMD1003 |
4.3 |
% |