| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.922 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
6.5 |
g/10min |
| 机械性能 |
抗张强度1,2(屈服) |
|
ASTMD638 |
7.00 |
MPa |
| 机械性能 |
抗张强度3(断裂) |
|
ASTMD638 |
8.00 |
MPa |
| 机械性能 |
弯曲模量-2%正割3 |
|
ASTMD790 |
232 |
MPa |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
TensileStrength-MD(Break,25µm) |
|
ASTMD882 |
18.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm) |
|
ASTMD882 |
18.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,25µm) |
|
ASTMD882 |
330 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm) |
|
ASTMD882 |
600 |
% |
| 薄膜 |
DartDropImpact4(25µm) |
|
ASTMD1709A |
60 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(25µm) |
|
ASTMD1922 |
350 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm) |
|
ASTMD1922 |
120 |
g |
| 热性能 |
脆化温度3 |
|
ASTMD746 |
-60.0 |
°C |
| 光学性能 |
光泽度(45°,25.0µm,吹塑薄膜) |
|
ASTMD2457 |
75 |
|
| 光学性能 |
雾度(25.0µm,吹塑薄膜) |
|
ASTMD1003 |
5.5 |
% |