| 规格级别 | 其它 其它 吹塑,挤出 | 外观颜色 | |
| 该料用途 | 薄膜 复合物 涂敷应用 铸造薄膜 | ||
| 备注说明 | 均聚物 良好的剥离性 韧性良好 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.920 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 7.0 |
g/10 min
|
|
| 机械性能 |
割线模量
|
1% 正割, MD
|
ASTM D882 | 165 |
MPa
|
|
1% 正割, TD
|
ASTM D882 | 200 |
MPa
|
||
|
抗张强度
|
MD: 屈服
|
ASTM D882 | 8.96 |
MPa
|
|
|
TD: 屈服
|
ASTM D882 | 8.96 |
MPa
|
||
|
MD: 断裂
|
ASTM D882 | 20.7 |
MPa
|
||
|
TD: 断裂
|
ASTM D882 | 17.9 |
MPa
|
||
|
伸长率
|
MD: 断裂
|
ASTM D882 | 390 | % | |
|
TD: 断裂
|
ASTM D882 | 680 | % | ||
|
落锤冲击
|
ASTM D1709A | 80 |
g
|
||
|
埃尔曼多夫抗撕强度
|
MD | ASTM D1922 | 440 |
g
|
|
|
TD
|
ASTM D1922 | 200 |
g
|
||
| 热性能 |
熔融峰值温度
|
No Standard | 109 | ℃ | |
| 光学性能 | 光泽度 | 45℃ | ASTM D2457 | 82 | |
|
雾度
|
ASTM D1003 | 4.0 | % | ||