LDPE | 6434F
生产厂家：台湾塑胶
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
薄透明膜 |
| 备注说明 |
光学性好 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
|
ASTM D-1238 |
3.5 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.924 |
g/cm3 |
| 物理性能 |
薄膜厚度 |
|
|
18-70 |
|
| 机械性能 |
断裂点强度 |
MD |
|
ASTM D-882B |
210 |
kg/cm2 |
| TD |
|
ASTM D-882B |
160 |
kg/cm2 |
| 断裂点伸长率 |
MD |
|
ASTM D-882B |
250 |
kg/cm2 |
| TD |
|
ASTM D-882B |
550 |
kg/cm2 |
| 降伏点强度 |
MD |
|
ASTM D-882B |
110 |
kg/cm2 |
| TD |
|
ASTM D-882B |
110 |
kg/cm2 |
| 热性能 |
软化点 |
|
ASTM D-1525 |
94 |
℃ |
| 熔点 |
|
DSC |
113 |
℃ |
| 脆化温度 |
|
ASTM D-746 |
<-75 |
℃ |
| 其它性能 |
摩擦系数 |
|
ASTM D-1894 |
0.11 |
|
| 1%伸长弹性系数 |
MD |
|
ASTM D-882B |
1900 |
kg/cm2 |
| TD |
|
ASTM D-882B |
2100 |
kg/cm2 |
| 浊度 |
|
ASTM D-1003 |
6.5 |
% |
| 抗撕裂性 |
MD |
|
ASTM D-1922 |
70 |
N/mm |
| TD |
|
ASTM D-1922 |
45 |
N/mm |
| 光泽度 |
45℃ |
ASTM D-2457 |
68 |
% |
| 落球冲击强度 |
|
ASTM D-1709 |
85 |
%｜% |
-
-