LDPE | 640I
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
薄膜级用 |
| 备注说明 |
产品商标DOW |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.920 |
g/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
2.0 |
g/10min |
| 薄膜厚度 |
|
|
50.8 |
μ |
| 机械性能 |
弯曲模量 |
|
ASTM D-790 |
234 |
MPa |
| 薄膜强度 |
MD |
|
ASTM D-882 |
159 |
J/cm3 |
| TD |
|
ASTM D-882 |
184 |
J/cm3 |
| 切割模量 |
MD |
|
ASTM D-882 |
181 |
MPa |
| TD |
|
ASTM D-882 |
207 |
MPa |
| 屈服拉伸强度 |
MD |
|
ASTM D-882 |
12.3 |
MPa |
| TD |
|
ASTM D-882 |
12.1 |
MPa |
| 断裂拉伸强度 |
MD |
|
ASTM D-882 |
24.8 |
MPa |
| TD |
|
ASTM D-882 |
23.0 |
MPa |
| 断裂伸长率 |
MD |
|
ASTM D-882 |
420 |
% |
| TD |
|
ASTM D-882 |
670 |
% |
| 落镖冲击强度 |
|
ASTM D-1709 |
150 |
g |
| 埃尔曼多夫撕裂强度 |
MD |
|
ASTM D-1922 |
500 |
g |
| TD |
|
ASTM D-1922 |
280 |
g |
| 拉伸冲击强度 |
|
ASTM D-1822 |
147 |
KJ/M2 |
| 硬度 |
|
ASTM D-2240 |
45 |
|
| 热性能 |
脆化温度 |
|
ASTM D-746 |
-76.1 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
95 |
℃ |
| 熔点 |
|
DSC |
112 |
℃ |
| 结晶点 |
|
ASTM D-3418 |
98.3 |
℃ |
| 其它性能 |
耐环境应力开裂性 |
|
ASTM D-1693 |
2.00 |
hr |
| DTUL |
|
ASTM D-648 |
38.3 |
℃ |
| 光学性能 |
光泽度 |
45° |
ASTM D-2457 |
66 |
|
| 雾度 |
|
ASTM D-1003 |
7.6 |
% |
-
-