| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 低密度、高光滑性、 可加工性，良好、一般目的、中等抗结块性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.924 |
g/cm³
|
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 2.1 |
g/10 min
|
|
| 硬度计硬度 | 支撐 D | ASTM D2240 | 53 | ||
| 机械性能 | 抗张强度 |
屈服
|
ASTM D638 | 9.81 |
MPa
|
|
断裂
|
ASTM D638 | 14.7 |
MPa
|
||
| 伸长率 | 断裂 | ASTM D638 | 600 | % | |
| 弯曲模量 | ASTM D790 | 177 |
MPa
|
||
| 摩擦系数 | 吹塑薄膜 | ASTM D1894 | 0.12 | ||
| 薄膜厚度 | 经测试 | 30 |
µm
|
||
| 可供应的薄膜厚度 | 1-3.1 | mil | |||
| 割线模量 |
1% 正割, MD: 38 µm, 吹塑薄膜
|
ASTM D882 | 196 |
MPa
|
|
|
1% 正割, TD: 38 µm, 吹塑薄膜
|
ASTM D882 | 226 |
MPa
|
||
| 抗张强度 |
MD: 屈服, 38 µm, 吹塑薄膜
|
ASTM D882 | 9.81 |
MPa
|
|
|
TD: 屈服, 38 µm, 吹塑薄膜
|
ASTM D882 | 10.8 |
MPa
|
||
|
MD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 22.6 |
MPa
|
||
|
TD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 17.7 |
MPa
|
||
| 伸长率 |
MD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 280 | % | |
|
TD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 580 | % | ||
| 落锤冲击 | 38 µm, 吹塑薄膜 | ASTM D1709 | 100 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD: 38 µm, 吹塑薄膜
|
ASTM D1922 | 240 |
g
|
|
|
TD: 38 µm, 吹塑薄膜
|
ASTM D1922 | 150 |
g
|
||
| 热性能 |
脆化温度 | ASTM D746 | -70.0 |
°C
|
|
| 维卡软化温度 | ASTM D1525 | 96.0 |
°C
|
||
| 熔融温度 | ASTM D1525 | 113 |
°C
|
||