LDPE | 6323F
生产厂家：台湾塑胶
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
一般包装膜、夹链袋、中空吹制、发泡缓冲材。 |
| 备注说明 |
特性：加工稳定佳、柔软性佳、架桥性。 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.918 |
g/cm3 |
| 熔体流动速率 |
MI2.16 |
ASTM D-1238 |
2.5 |
℃ |
| 物理性能 |
光泽度 |
45℃ |
ASTM D-2457 |
60 |
% |
| 膜厚度 |
|
|
25-80 |
μ |
| 摩擦系数 |
|
ASTM D-1894 |
<0.13 |
|
| 机械性能 |
拉力断裂伸长率 |
MD |
|
ASTM D-882B |
250 |
% |
| TD |
|
ASTM D-882B |
550 |
% |
| 弯曲模量 |
|
ASTM D-790 |
1700 |
kg/cm2 |
| 拉力断裂强度 |
MD |
|
ASTM D-882B |
210 |
KG/cm2 |
| TD |
|
ASTM D-882B |
170 |
KG/cm2 |
| 抗撕裂性 |
MD |
|
ASTM D-1922 |
70 |
N/mm |
| TD |
|
ASTM D-1922 |
50 |
N/mm |
| 落球冲击强度 |
|
ASTM D-1709 |
100 |
g |
| 拉力降伏强度 |
MD |
|
ASTM D-882B |
100 |
KG/cm2 |
| TD |
|
ASTM D-882B |
110 |
KG/cm2 |
| 拉力断裂强度 |
|
ASTM D-638 |
150 |
kg/cm2 |
| 硬度 |
|
ASTM D-2240 |
52 |
Shore D |
| 拉力降伏强度 |
|
ASTM D-638 |
100 |
kg/cm2 |
| 拉力断裂伸长率 |
|
ASTM D-638 |
600 |
% |
| 1%伸长弹性系数 |
MD |
|
ASTM D-882B |
1900 |
KG/cm2 |
| TD |
|
ASTM D-882B |
2200 |
KG/cm2 |
| 热性能 |
脆化温度 |
|
ASTM D-746 |
＜-70 |
℃ |
| 熔点 |
|
DSC |
107 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
95 |
℃ |
| 其它性能 |
浊度 |
|
ASTM D-1003 |
13 |
% |
-
-