LDPE | 6320F
生产厂家：台湾塑胶
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
一般薄膜 |
| 备注说明 |
具有良好的加工性和机械性 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
|
ASTM D-1238 |
2.2 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.921 |
g/cm3 |
| 物理性能 |
薄膜厚度 |
|
|
30-80 |
|
| 机械性能 |
断裂点伸长率 |
MD |
|
ASTM D-882B |
240 |
% |
| TD |
|
ASTM D-882B |
600 |
% |
| 落球冲击强度 |
|
ASTM D-1709 |
115 |
g |
| 降伏点强度 |
MD |
|
ASTM D-882B |
100 |
kg/cm2 |
| TD |
|
ASTM D-882B |
110 |
kg/cm2 |
| 断裂点强度 |
MD |
|
ASTM D-882B |
250 |
kg/cm2 |
| TD |
|
ASTM D-882B |
190 |
kg/cm2 |
| 热性能 |
软化点 |
|
ASTM D-1525 |
93 |
℃ |
| 脆化温度 |
|
ASTM D-746 |
<-75 |
℃ |
| 熔点 |
|
DSC |
111 |
℃ |
| 其它性能 |
抗撕裂性 |
MD |
|
ASTM D-1922 |
70 |
N/mm |
| TD |
|
ASTM D-1922 |
45 |
N/mm |
| 摩擦系数 |
|
ASTM D-1894 |
>0.5 |
|
| 浊度 |
|
ASTM D-1003 |
8 |
% |
| 1%伸长弹性系数 |
MD |
|
ASTM D-882B |
1500 |
kg/cm2 |
| TD |
|
ASTM D-882B |
1700 |
kg/cm2 |
| 光泽度 |
45℃ |
ASTM D-2457 |
60 |
% |
-
-