LDPE | 608A
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
薄膜级用 |
| 备注说明 |
产品商标DOW |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.923 |
g/cm3 |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
2.6 |
g/10min |
| 薄膜厚度 |
|
|
50.8 |
μ |
| 机械性能 |
屈服拉伸强度 |
MD |
|
ASTM D-882 |
12.5 |
MPa |
| TD |
|
ASTM D-882 |
12.7 |
MPa |
| 断裂拉伸强度 |
MD |
|
ASTM D-882 |
23.4 |
MPa |
| TD |
|
ASTM D-882 |
20.6 |
MPa |
| 断裂伸长率 |
MD |
|
ASTM D-882 |
580 |
% |
| TD |
|
ASTM D-882 |
780 |
% |
| 落镖冲击强度 |
|
ASTM D-1709 |
87 |
g |
| 埃尔曼多夫撕裂强度 |
MD |
|
ASTM D-1922 |
450 |
g |
| TD |
|
ASTM D-1922 |
430 |
g |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
97.2 |
℃ |
| 熔点 |
|
DSC |
113 |
℃ |
| 其它性能 |
薄膜强度 |
MD |
|
ASTM D-882 |
186 |
J/cm3 |
| TD |
|
ASTM D-882 |
207 |
J/cm3 |
| 光学性能 |
光泽度 |
45° |
ASTM D-2457 |
81 |
|
| 雾度 |
|
ASTM D-1003 |
5.7 |
% |
-
-