LDPE | 6030F
生产厂家：台湾塑胶
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
用途：重包装膜、工业收缩膜、产业用膜、物理发泡。 |
| 备注说明 |
特性：机械性质佳。 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
MI2.16 |
ASTM D-1238 |
0.27 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.922 |
g/cm3 |
| 机械性能 |
1%伸长弹性系数 |
MD |
|
ASTM D-882B |
1700 |
kg/cm2 |
| TD |
|
ASTM D-882B |
1900 |
kg/cm2 |
| 拉力断裂强度 |
MD |
|
ASTM D-882B |
250 |
kg/cm2 |
| TD |
|
ASTM D-882B |
220 |
kg/cm2 |
| 拉力降伏强度 |
|
ASTM D-638 |
95 |
kg/cm2 |
| 抗撕裂性 |
MD |
|
ASTM D-1922 |
40 |
N/mm |
| TD |
|
ASTM D-1922 |
50 |
N/mm |
| 拉力断裂伸长率 |
|
ASTM D-638 |
700 |
% |
| 硬度 |
|
ASTM D-2240 |
51 |
Shore D |
| 拉力断裂强度 |
|
ASTM D-638 |
190 |
kg/cm2 |
| 拉力降伏强度 |
MD |
|
ASTM D-882B |
100 |
kg/cm2 |
| TD |
|
ASTM D-882B |
100 |
kg/cm2 |
| 摩擦系数 |
|
ASTM D-1894 |
>0.5 |
|
| 拉力断裂伸长率 |
MD |
|
ASTM D-882B |
380 |
% |
| TD |
|
ASTM D-882B |
580 |
% |
| 弯曲模量 |
|
ASTM D-790 |
1500 |
kg/cm2 |
| 落球行动强度 |
|
ASTM D-1709 |
260 |
g |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
96 |
℃ |
| 熔点 |
|
DSC |
113 |
℃ |
| 脆化温度 |
|
ASTM D-746 |
<-70 |
℃ |
| 其它性能 |
建设薄膜厚度 |
|
|
50～250 |
µ |
| 浊度 |
|
ASTM D-1003 |
15 |
% |
| 光泽度 |
|
ASTM D-2457 |
50 |
% |
-
-