HIPS | 55-WC
生产厂家：LG化学
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
耐磨性 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
熔体流动速率 |
200℃/5Kg |
ASTM D-1238 |
3 |
g/10min |
| 成型收缩率 |
|
ASTM D-955 |
0.4～0.8 |
% |
| 比重 |
|
ASTM D-792 |
1.04 |
|
| 机械性能 |
延伸率 |
|
ASTM D-638 |
40 |
% |
| 抗张强度 |
|
ASTM D-638 |
380 |
kg/cm2 |
| 弯曲弹性率 |
|
ASTM D-790 |
650 |
kg/cm2 |
| 冲击强度 |
Notched 1/4" |
ASTM D-256 |
5 |
Kg/cm/cm |
| 冲击强度 |
Notched1/8" |
ASTM D-256 |
75 |
Kg/cm/cm |
| 洛氏硬度 |
R-Scale |
ASTM D-785 |
110 |
|
| 挠曲模量 |
|
ASTM D-790 |
27.000 |
kg/cm2 |
| 电气性能 |
HWI |
|
UL 746A |
3 |
PLC |
| 抗弧光 |
|
ASTM D-495 |
5 |
PLC |
| HAI |
|
UL 746A |
0 |
PLC |
| CTI |
|
UL 746A |
1 |
PLC |
| HVTR |
|
UL 746A |
3 |
PLC |
| 热性能 |
维卡软化点 |
1.000g |
ASTM D-1525 |
101 |
℃ |
| 燃烧率 |
1/16" |
UL 94 |
HB |
|
| 热变形温度 |
Unannealed18.5g/cm2,1/4" |
ASTM D-648 |
80 |
℃ |
| 燃烧率 |
1/8" |
UL 94 |
HB |
|
| 燃烧率 |
1/8" |
IEC 707 |
FH3-30 |
mm/min |
-
-