HIPS | 55-SH
生产厂家：LG化学
规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
成型收缩率 |
|
ASTM D-955 |
0.4～0.8 |
% |
| 熔体流动速率 |
200℃/5Kg |
ASTM D-1238 |
3.5 |
g/10min |
| 比重 |
|
ASTM D-792 |
1.04 |
|
| 机械性能 |
延伸率 |
|
ASTM D-638 |
50 |
% |
| 挠曲模量 |
|
ASTM D-790 |
22.000 |
kg/cm2 |
| 冲击强度 |
Notched1/4" |
ASTM D-256 |
8 |
Kg/cm/cm |
| 抗张强度 |
|
ASTM D-638 |
320 |
kg/cm2 |
| 冲击强度 |
Notched1/8" |
ASTM D-256 |
11 |
Kg/cm/cm |
| 洛氏硬度 |
R-Scale |
ASTM D-785 |
99 |
|
| 弯曲弹性率 |
|
ASTM D-790 |
550 |
kg/cm2 |
| 电气性能 |
CTI |
|
UL 746A |
1 |
PLC |
| HWI |
|
UL 746A |
3 |
PLC |
| HVTR |
|
UL 746A |
2 |
PLC |
| 抗弧光 |
|
ASTM D-495 |
6 |
PLC |
| HAI |
|
UL 746A |
0 |
PLC |
| 热性能 |
燃烧率 |
1/8" |
IEC 707 |
FH3-30 |
mm/min |
| 燃烧率 |
1/16" |
UL 94 |
HB |
|
| 热变形温度 |
Unannealed18.5g/cm2,1/4" |
ASTM D-648 |
77 |
℃ |
| 燃烧率 |
1/8" |
UL 94 |
HB |
|
| 维卡软化点 |
1.000g |
ASTM D-1525 |
97 |
℃ |
-
-