| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
3.5 |
g/10min |
| 物理性能 |
比重 |
|
ASTM D-792 |
0.941 |
g/cm3 |
| 机械性能 |
环境应力开裂 |
Compression Molded |
ASTM D-1693B |
>1000 |
hr |
| 邵氏硬度 |
Shore D，Compression Molded |
ASTM D-2240 |
61 |
|
| 拉伸屈服强度 |
1.9mm，Compression Molded |
ASTM D-638 |
20.2 |
MPa |
| 拉伸断裂强度 |
1.9mm，Compression Molded |
ASTM D-638 |
29.3 |
MPa |
| 拉伸屈服伸长率 |
1.9mm，Compression Molded |
ASTM D-638 |
12 |
% |
| 拉伸断裂伸长率 |
1.9mm，Compression Molded |
ASTM D-638 |
900 |
% |
| 弯曲模量-1% Secant |
Compression Molded |
ASTM D-790 |
827 |
MPa |
| 热性能 |
热变形温度 |
0.45MPa，Unannealed，Compression Molded |
ASTM D-648 |
60 |
℃ |
| 热变形温度 |
1.8MPa，Unannealed，Compression Molded |
ASTM D-648 |
43 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
123 |
℃ |
| 熔化温度 |
|
ASTM E-794 |
125 |
℃ |