| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.947 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率） | 190°C/2.16kg | ASTMD1238 | 0.28 | g/10min |
| 物理性能 | 熔流率（熔体流动速率） | 190°C/21.6kg | ASTMD1238 | 20 | g/10min |
| 薄膜 | 薄膜厚度-经测试 | 25 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(25µm,BlownFilm) | ASTMD882A | 710 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(25µm,BlownFilm) | ASTMD882A | 1000 | MPa | |
| 薄膜 | 抗张强度-MD | Yield,25µm,BlownFilm2 | ASTMD882A | 24.1 | MPa |
| 薄膜 | 抗张强度-MD | Yield,25µm,BlownFilm | ASTMD882A | 23.4 | MPa |
| 薄膜 | TensileStrength-TD | Yield,25µm,BlownFilm2 | ASTMD882A | 25.5 | MPa |
| 薄膜 | TensileStrength-TD | Yield,25µm,BlownFilm | ASTMD882A | 26.2 | MPa |
| 薄膜 | 抗张强度-MD | Break,25µm,BlownFilm2 | ASTMD882A | 54.5 | MPa |
| 薄膜 | 抗张强度-MD | Break,25µm,BlownFilm | ASTMD882A | 62.1 | MPa |
| 薄膜 | TensileStrength-TD | Break,25µm,BlownFilm2 | ASTMD882A | 39.3 | MPa |
| 薄膜 | TensileStrength-TD | Break,25µm,BlownFilm | ASTMD882A | 18.6 | MPa |
| 薄膜 | 伸长率-MD | Break,25µm,BlownFilm2 | ASTMD882A | 600 | % |
| 薄膜 | 伸长率-MD | Break,25µm,BlownFilm | ASTMD882A | 450 | % |
| 薄膜 | TensileElongation-TD | Break,25µm,BlownFilm2 | ASTMD882A | 700 | % |
| 薄膜 | TensileElongation-TD | Break,25µm,BlownFilm | ASTMD882A | 600 | % |
| 薄膜 | 落锤冲击 | 25µm,BlownFilm2 | ASTMD1709A | 100 | g |
| 薄膜 | 落锤冲击 | 25µm,吹塑薄膜 | ASTMD1709A | <50 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 25µm,BlownFilm2 | ASTMD1922 | 28 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 25µm,吹塑薄膜 | ASTMD1922 | 10 | g |
| 薄膜 | ElmendorfTearStrength-TD | 25µm,BlownFilm2 | ASTMD1922 | 530 | g |
| 薄膜 | ElmendorfTearStrength-TD | 25µm,吹塑薄膜 | ASTMD1922 | 1500 | g |
| 薄膜 | 水气透过率 | 25µm,BlownFilm2 | ASTMF1249 | 7.8 | g/m²/24hr |
| 薄膜 | 水气透过率 | 25µm,吹塑薄膜 | ASTMF1249 | 11 | g/m²/24hr |
| 热性能 | 熔融峰值温度 | ASTMD3417 | 131 | °C | |