| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.950 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/2.16kg |
ASTMD1238 |
0.080 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg |
ASTMD1238 |
11 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/5.0kg |
ASTMD1238 |
0.32 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
20 |
µm |
| 薄膜 |
SecantModulus-2%Secant,MD2(20µm,BlownFilm) |
|
ASTMD882A |
841 |
MPa |
| 薄膜 |
SecantModulus-2%Secant,TD2(20µm,BlownFilm) |
|
ASTMD882A |
910 |
MPa |
| 薄膜 |
TensileStrength-MD2(Yield,20µm,BlownFilm) |
|
ASTMD882A |
36.5 |
MPa |
| 薄膜 |
TensileStrength-TD2(Yield,20µm,BlownFilm) |
|
ASTMD882A |
34.5 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,20µm,BlownFilm) |
|
ASTMD882A |
63.4 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,20µm,BlownFilm) |
|
ASTMD882A |
67.6 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,20µm,BlownFilm) |
|
ASTMD882A |
300to500 |
% |
| 薄膜 |
TensileElongation-TD2(Break,20µm,BlownFilm) |
|
ASTMD882A |
300to500 |
% |
| 薄膜 |
落锤冲击(20µm,吹塑薄膜) |
|
ASTMD1709A |
350 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(20µm,BlownFilm) |
|
ASTMD1922 |
24 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(20µm,BlownFilm) |
|
ASTMD1922 |
120 |
g |
| 薄膜 |
水蒸气透过性3 |
|
ASTME96 |
12 |
g/m²/24hr |
| 热性能 |
熔融峰值温度 |
|
ASTMD3417 |
127 |
°C |