| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.967 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.2 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(38µm,BlownFilm) |
|
ASTMD882 |
1100 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(38µm,BlownFilm) |
|
ASTMD882 |
1340 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,38µm,BlownFilm) |
|
ASTMD882 |
27.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,38µm,BlownFilm) |
|
ASTMD882 |
25.0 |
MPa |
| 薄膜 |
ElmendorfTearStrength-MD(38µm,BlownFilm) |
|
ASTMD1922 |
22 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) |
|
ASTMD1922 |
230 |
g |
| 薄膜 |
OxygenTransmissionRate(23°C,0%RH) |
|
ASTMD3985 |
470 |
cm³/m²/24hr |
| 薄膜 |
水气透过率(38°C,100%RH) |
|
ASTMF1249 |
1.1 |
g·mm/m²/atm/24hr |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
LowFrictionPuncture2(38.0µm) |
|
InternalMethod |
190 |
J/cm |