HDPE | SF 5007
生产厂家：印尼钱德拉阿斯里
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
衬里，袋子，工业领域：包装，薄膜 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTM D1505 |
0.950 |
g/cm³ |
| 熔流率 |
190℃/2.16 kg
|
ASTM D1238 |
0.050 |
g/10 min |
| 190℃/21.6 kg |
ASTM D1238 |
15 |
g/10 min |
| 抗环境应力开裂 |
F50 |
ASTM D1693 |
> 500 |
hr |
| 机械性能 |
弯曲模量 |
|
ASTM D790 |
1100
|
MPa |
| 薄膜厚度 - 经测试 |
|
|
20 |
µm |
| 弹性模量 - MD |
20 µm, 吹塑薄膜 |
ASTM D882 |
850 |
MPa |
弹性模量 - TD
|
20 µm, 吹塑薄膜 |
ASTM D882 |
1050 |
MPa |
| 抗张强度 |
MD: 断裂, 20 µm, 吹塑薄膜 |
ASTM D882 |
100 |
MPa |
| TD: 断裂, 20 µm, 吹塑薄膜 |
ASTM D882 |
55.0 |
MPa |
| 伸长率 |
MD: 断裂, 20 µm, 吹塑薄膜 |
ASTM D882 |
500 |
% |
| TD: 断裂, 20 µm, 吹塑薄膜 |
ASTM D882 |
700 |
% |
| 落锤冲击 |
20 µm, 吹塑薄膜 |
ASTM D1709 |
130 |
g |
| Elmendorf Tear Strength |
MD: 20.0 µm, Blown Film |
ASTM D1922 |
6.9 |
kN/m |
| TD: 20.0 µm, Blown Film |
ASTM D1922 |
147.1 |
kN/m |
Impact Strength
|
20.0 µm, Blown Film |
ASTM D3420 |
34.3 |
J/cm |
| 热性能 |
脆化温度 |
|
ASTM D746 |
< -70.0 |
℃ |
| 维卡软化温度 |
|
ASTM D1525 |
127 |
℃ |
| 熔体温度 |
|
|
180-220 |
℃ |
-
-