| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.949 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.33 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(51µm) |
|
ASTME111 |
758 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(51µm) |
|
ASTME111 |
924 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,51µm) |
|
ASTMD882 |
24.8 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,51µm) |
|
ASTMD882 |
28.3 |
MPa |
| 薄膜 |
抗张强度-MD(断裂,50µm) |
|
ASTMD882 |
43.4 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,51µm) |
|
ASTMD882 |
31.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,50µm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm) |
|
ASTMD882 |
670 |
% |
| 薄膜 |
DartDropImpact(51µm,BlownFilm) |
|
ASTMD1709 |
70 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(51µm,BlownFilm) |
|
ASTMD1922 |
31 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(51µm,BlownFilm) |
|
ASTMD1922 |
1200 |
g |
| 薄膜 |
氧气传输速率(51µm,吹塑薄膜) |
|
ASTMD3985 |
2400 |
cm³/m²/24hr |
| 薄膜 |
水蒸气透过性2 |
|
ASTMF372 |
3.3 |
g/m²/24hr |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
126 |
°C |