| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.946 |
g/m3 |
| 熔体流动速率 |
190℃/5.0kg |
ASTM D-1238 |
7.6 |
g/10min |
| 机械性能 |
环境应力开裂 |
50℃，2.00mm，10% Igepal，Compression Molded，F50 |
ASTM D-1693B |
1.8 |
hr |
| 拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
22 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ASTM D-638 |
13 |
MPa |
| 拉伸屈服伸长率 |
Compression Molded |
ASTM D-638 |
13 |
% |
| 拉伸断裂伸长率 |
Compression Molded |
ASTM D-638 |
860 |
% |
| 弯曲模量 |
Compression Molded |
ASTM D-790 |
780 |
MPa |
| IZOD缺口冲击强度 |
Compression Molded |
ASTM D-256 |
51 |
J/m |
| 邵氏硬度 |
Shore D，Compression Molded |
ASTM D-2240 |
57 |
|
| 热性能 |
负荷弯曲温度 |
0.45MPa，Unannealed，Compression Molded |
ASTM D-648 |
62 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
120 |
℃ |