| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.944 |
g/cm3 |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
0.06 |
g/10min |
| 熔体流动速率 |
190℃/21.6kg |
ASTM D-1238 |
8 |
g/10min |
| 机械性能 |
环境开裂应力 |
100% Igepal，Compression Molded，F50 |
ASTM D-1693A |
1000 |
hr |
| 环境开裂应力 |
100% Igepal，Compression Molded，F50 |
ASTM D-1693B |
1000 |
hr |
| 环境开裂应力 |
100% Igepal，Compression Molded，F50 |
ASTM D-1693C |
1000 |
hr |
| 拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
22.1 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ASTM D-638 |
34.5 |
MPa |
| 拉伸断裂伸长率 |
Compression Molded |
ASTM D-638 |
500 |
% |
| 弯曲模量 |
Compression Molded |
ASTM D-790 |
965 |
MPa |
| 热性能 |
维卡软化点 |
|
ASTM D-746 |
-90 |
℃ |