| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.948 |
g/cm3 |
| 熔体流动速率 |
190℃/21.6kg |
ASTM D-1238 |
10 |
g/10min |
| 薄膜厚度-Tested |
|
|
12.5 |
um |
| 机械性能 |
环境应力开裂 |
50℃，100% Igepal，Compression Molded，F50 |
ASTM D-1693 |
>1000 |
hr |
| 拉伸模量-1% Secant |
Compression Molded |
ASTM D-638 |
537 |
MPa |
| 拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
25 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ASTM D-638 |
27 |
MPa |
| 拉伸断裂伸长率 |
Compression Molded |
ASTM D-638 |
1300 |
% |
| 拉伸屈服伸长率 |
Compression Molded |
ASTM D-638 |
10 |
% |
| 弯曲模量 |
Compression Molded |
ASTM D-790 |
963 |
MPa |
| 割线模量-1% Secant |
12.5um，Blown Film |
ASTM D-882 |
|
MPa |
| 拉伸屈服强度 |
12.5um，Blown Film |
ASTM D-882 |
|
MPa |
| 拉伸断裂强度 |
12.5um，Blown Film |
ASTM D-882 |
|
MPa |
| 拉伸屈服伸长率 |
12.5um，Blown Film |
ASTM D-882 |
|
% |
| 拉伸断裂伸长率 |
12.5um，Blown Film |
ASTM D-882 |
|
% |
| 落锤冲击 |
12.5um，Blown Film |
ASTM D-1709A |
140 |
g |
| IZOD缺口冲击强度 |
Compression Molded |
ASTM D-256 |
224 |
J/m |
| 邵氏硬度 |
Shore D，Compression Molded |
ASTM D-2240 |
61 |
|
| 热性能 |
热变形温度 |
0.45MPa，Unannealed，Compression Molded |
ASTM D-648 |
60 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
125 |
℃ |