| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.951 |
g/m3 |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
0.3 |
g/10min |
| 熔体流动速率 |
190℃/21.6kg |
ASTM D-1238 |
29 |
g/10min |
| 机械性能 |
环境应力开裂 |
50℃，10% Igepal，Compression Molded，F50 |
ASTM D-1693 |
22 |
hr |
| 拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
26 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ASTM D-638 |
32 |
MPa |
| 弯曲模量 |
Compression Mold |
ASTM D-790A |
1140 |
MPa |
| 邵氏硬度 |
Shore D, Compression Molded |
ASTM D-2240 |
63 |
|
| 邵氏硬度 |
Shore D，Compression Molded |
ASTM D-2240 |
63 |
|
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
125 |
℃ |
| 负荷弯曲温度 |
0.45MPa，Unannealed，Compression Molded |
ASTM D-648 |
67 |
|