| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.949 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/2.16kg2 |
ASTMD1238 |
0.040 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg3 |
ASTMD1238 |
8.0 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
13 |
µm |
| 薄膜 |
TensileStrength-MD(Break,13µm) |
|
ASTMD882 |
60.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,13µm) |
|
ASTMD882 |
31.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,13µm) |
|
ASTMD882 |
330 |
% |
| 薄膜 |
TensileElongation-TD(Break,13µm) |
|
ASTMD882 |
460 |
% |
| 薄膜 |
DartDropImpact(13µm) |
|
ASTMD1709 |
300 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(13µm) |
|
ASTMD1922 |
18 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(13µm) |
|
ASTMD1922 |
35 |
g |
| 热性能 |
熔融温度 |
|
DSC |
131 |
°C |