| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 0.955 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 1.5 |
g/10 min
|
|
| 抗环境应力开裂 | 50℃, 10% Igepal, F50 | ASTM D1693 | 272 | hr | |
|
50℃
, 100% Igepal, F50
|
ASTM D1693 |
> 1000
|
hr | ||
| 硬度计硬度 | 邵氏 D | ASTM D2240 | 60 | ||
| 机械性能 | 抗张强度 | 屈服 | ASTM D638 | 28.0 |
MPa
|
| 断裂 | ASTM D638 | 22.0 |
MPa
|
||
| 伸长率 | 屈服 | ASTM D638 | 9.0 | % | |
| 断裂 | ASTM D638 | 690 | % | ||
| 弯曲模量 | 2% 正割 | ASTM D790B | 1100 |
MPa
|
|
| 热性能 | 热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 69.0 | ℃ |
| 维卡软化温度 | ASTM D1525 | 128 | ℃ | ||
| 溶融温度 | DSC | Internal Method | 130 | ℃ | |
| 结晶峰温 | DSC | Internal Method | 117 | ℃ | |