HDPE | DGDC-2100 NT 7
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
挤压，吹薄用 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.950 |
g/cm3 |
| 熔体流动速率 |
190℃/21.6kg |
ASTM D-1238 |
9.0 |
g/10min |
| 薄膜厚度 |
|
|
0.500 |
mil |
| 熔点 |
|
DSC |
128 |
℃ |
| 机械性能 |
切割模量 |
MD |
|
ASTM D-882 |
965.2 |
MPa |
| TD |
|
ASTM D-882 |
1096.2 |
MPa |
| 屈服拉伸强度 |
MD |
|
ASTM D-882 |
42.3 |
MPa |
| TD |
|
ASTM D-882 |
31.7 |
MPa |
| 断裂拉伸强度 |
MD |
|
ASTM D-882 |
93.7 |
MPa |
| TD |
|
ASTM D-882 |
68.8 |
MPa |
| 断裂伸长率 |
MD |
|
ASTM D-882 |
330 |
% |
| TD |
|
ASTM D-882 |
410 |
% |
| 缺口冲击强度 |
|
ASTM D-1709 |
350 |
g |
| 埃尔曼多夫撕裂强度 |
MD |
|
ASTM D-1922 |
11 |
g |
| TD |
|
ASTM D-1922 |
73 |
g |
| 光学性能 |
光泽度 |
|
ASTM D-2457 |
9 |
|
| 雾度 |
|
ASTM D-1003 |
69 |
% |
-
-