| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.952 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/2.16kg |
ASTMD1238 |
0.050 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg |
ASTMD1238 |
8.0 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
10 |
µm |
| 薄膜 |
可供应的薄膜厚度 |
|
|
Minimum10µm(0.4mil) |
|
| 薄膜 |
SecantModulus-1%Secant,MD |
|
ASTMD882 |
790 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
|
ASTMD882 |
965 |
MPa |
| 薄膜 |
抗张强度-MD(屈服) |
|
ASTMD882 |
28.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield) |
|
ASTMD882 |
26.0 |
MPa |
| 薄膜 |
抗张强度-MD(断裂) |
|
ASTMD882 |
69.0 |
MPa |
| 薄膜 |
抗张强度-TD(断裂) |
|
ASTMD882 |
41.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂) |
|
ASTMD882 |
330 |
% |
| 薄膜 |
TensileElongation-TD(Break) |
|
ASTMD882 |
480 |
% |
| 薄膜 |
落锤冲击6 |
|
ASTMD1709A |
280 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
|
ASTMD1922 |
20 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
|
ASTMD1922 |
200 |
g |
| 热性能 |
熔融峰值温度 |
|
ASTMD3417 |
129 |
°C |