| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.957 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.40 |
g/10min |
| 物理性能 |
EnvironmentalStress-CrackingResistance2(50°C,1.75mm,100%Igepal,CompressionMolded,F50) |
|
ASTMD1693B |
>900 |
hr |
| 物理性能 |
BulkDensity |
|
|
0.560 |
g/l |
| 机械性能 |
抗张强度3(屈服,模压成型) |
|
ASTMD638 |
28.0 |
MPa |
| 机械性能 |
伸长率3(断裂,模压成型) |
|
ASTMD638 |
1100 |
% |
| 机械性能 |
FlexuralModulus-1%Secant4(CompressionMolded) |
|
ASTMD790 |
1520 |
MPa |
| 冲击性能 |
拉伸冲击强度(模压成型) |
|
ASTMD1822 |
250 |
kJ/m² |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
76.0 |
°C |
| 热性能 |
脆化温度 |
|
ASTMD746 |
<-80.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
128 |
°C |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
BlowMoldingMoldTemperature |
|
|
10to30 |
°C |
| ADDITIONAL INFORMATION |
吹气模制温度 |
|
|
150to170 |
°C |