| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.952 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg |
ASTMD1238 |
9.3 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/5.0kg |
ASTMD1238 |
0.33 |
g/10min |
| 薄膜 |
SecantModulus-1%Secant,MD(13µm,BlownFilm) |
|
ASTMD882 |
750 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(13µm,BlownFilm) |
|
ASTMD882 |
870 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,13µm,BlownFilm) |
|
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,13µm,BlownFilm) |
|
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,13µm,BlownFilm) |
|
ASTMD882 |
85.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,13µm,BlownFilm) |
|
ASTMD882 |
45.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Yield,13µm,BlownFilm) |
|
ASTMD882 |
15 |
% |
| 薄膜 |
TensileElongation-TD(Yield,13µm,BlownFilm) |
|
ASTMD882 |
5.0 |
% |
| 薄膜 |
TensileElongation-MD(Break,13µm,BlownFilm) |
|
ASTMD882 |
590 |
% |
| 薄膜 |
TensileElongation-TD(Break,13µm,BlownFilm) |
|
ASTMD882 |
740 |
% |
| 薄膜 |
DartDropImpact(13µm,BlownFilm) |
|
ASTMD1709 |
200 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(13µm,BlownFilm) |
|
ASTMD1922 |
5.0 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(13µm,BlownFilm) |
|
ASTMD1922 |
50 |
g |
| 薄膜 |
SealInitiationTemperature(13µm,BlownFilm) |
|
|
125 |
°C |