| 规格级别 | 其它 其它 注塑 | 外观颜色 | 黑色,自然色 |
| 该料用途 | 强化玻璃纤维增强,30%填料重量,硅润滑油添加剂（2.0%） | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重 | ASTM D-792 | 1.18 | g/cm3 | |
| 成型收缩率 | 3.18mm | ASTM D-955 | 0.20 | % | |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.020 | % | |
| 机械性能 |
抗压强度 | ASTM D-695 | 48.3 | MPa | |
| 洛氏硬度 | R-Scale | ASTM D-785 | 75 | ||
| 拉伸模量 | ASTM D-638 | 5520 | MPa | ||
| 拉伸强度 | ASTM D-638 | 58.6 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 6.5 | % | ||
| 弯曲模量 | ASTM D-790 | 3450 | MPa | ||
| 弯曲强度 | ASTM D-790 | 75.8 | MPa | ||
| IZOD缺口冲击强度 | 3.18mm | ASTM D-256 | 133 | J/m | |
| IZOD无缺口冲击强度 | 3.18mm | ASTM D-256 | 641 | J/m | |
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D-648 | 129 |
℃
|
| 热变形温度 | 1.8MPa,未退火 | ASTM D-648 | 121 | ℃ | |
| 阻燃等级 | 1.59mm | UL 94 |
HB
|
||
| CLTE | ASTM D-696 |
0.000049
|
cm/cm/℃
|
||
| 导热 | ASTM C-177 |
0.36
|
W/m/K | ||
| 电气性能 | 介电强度 | ASTM D-149 | 20 |
kV/mm
|
|
| 介电常数 | 1 MHz | ASTM D-150 | 2.7 | ||
| 耗散因子 | 1 MHz | ASTM D-150 | 0.0070 | ||
| 电弧电阻 | ASTM D-495 | 140 |
sec
|
||
| 体积电阻率 | ASTM D-257 | 1.0E+16 | ohm·cm | ||