| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.19 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53478 |
1.19 |
g/cm³ |
| 物理性能 |
MeltVolume-FlowRate(MVR)(177°C/2.16kg) |
|
|
8.00 |
cm³/10min |
| 机械性能 |
Abrasion2 |
-- |
ASTMD395 |
51 |
mm³ |
| 机械性能 |
Abrasion2 |
-- |
DIN53516 |
50 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
ASTMD412 |
2.34 |
MPa |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
DIN53504 |
2.00 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
ASTMD412 |
4.83 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
DIN53504 |
5.00 |
MPa |
| ELASTOMERS |
TensileStrength3(Break,0.635mm) |
|
ASTMD412 |
41.4 |
MPa |
| ELASTOMERS |
TensileStress3(Break,0.635mm) |
|
DIN53504 |
42.0 |
MPa |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
ASTMD412 |
700 |
% |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
DIN53504 |
700 |
% |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
ASTMD624 |
66.5 |
kN/m |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
DIN53515 |
72 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,70hr |
ASTMD395 |
40 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
90 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,70hr |
DIN53517 |
40 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
DIN53517 |
90 |
% |
| ELASTOMERS |
巴肖氏弹性2 |
|
ASTMD2632 |
50 |
% |
| 硬度 |
肖氏硬度(邵氏A,注塑) |
|
ASTMD2240 |
78 |
|
| 硬度 |
ShoreHardness(ShoreA,InjectionMolded) |
|
DIN53505 |
78 |
|
| 热性能 |
TMA3 |
High:635.0µm |
InternalMethod |
130 |
°C |
| 热性能 |
TMA3 |
Low:635.0µm |
InternalMethod |
110 |
°C |