TPU | IROGRAN® A 92 H 4656
生产厂家：美国亨斯迈
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
|
1.21 |
g/cm³ |
| 物理性能 |
收缩率-流动(注塑) |
|
ASTMD955 |
0.60 |
% |
| 物理性能 |
收缩率2 |
|
|
0.40 |
% |
| 机械性能 |
Abrasion2 |
|
ISO4649 |
30 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
拉伸应力2(100%应变) |
|
ASTMD412 |
4.90 |
MPa |
| ELASTOMERS |
拉伸应力2(100%应变) |
|
DIN53504 |
9.00 |
MPa |
| ELASTOMERS |
拉伸应力2(300%应变) |
|
ASTMD412 |
11.0 |
MPa |
| ELASTOMERS |
拉伸应力2(300%应变) |
|
DIN53504 |
21.0 |
MPa |
| ELASTOMERS |
抗张强度2(断裂) |
|
ASTMD412 |
36.0 |
MPa |
| ELASTOMERS |
拉伸应力2(断裂) |
|
DIN53504 |
45.0 |
MPa |
| ELASTOMERS |
伸长率2(断裂) |
|
ASTMD412 |
750 |
% |
| ELASTOMERS |
伸长率2(断裂) |
|
DIN53504 |
550 |
% |
| ELASTOMERS |
撕裂强度2 |
|
ASTMD624 |
99.8 |
kN/m |
| ELASTOMERS |
撕裂强度2 |
|
ISO34-1 |
120 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ASTMD395 |
25 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
40 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ISO815 |
25 |
% |
| ELASTOMERS |
压缩永久变形2 |
73°C,24hr |
ISO815 |
40 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ASTMD2240 |
85 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ASTMD2240 |
34 |
|
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ISO868 |
92 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ISO868 |
40 |
|
-
-