| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.21 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53479 |
1.21 |
g/cm³ |
| 物理性能 |
MeltVolume-FlowRate(MVR)(190°C/10.0kg) |
|
|
60.0 |
cm³/10min |
| 机械性能 |
Abrasion2 |
|
DIN53516 |
20 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
拉伸应力2(100%应变) |
|
ASTMD412 |
6.69 |
MPa |
| ELASTOMERS |
拉伸应力2(100%应变) |
|
DIN53504 |
6.00 |
MPa |
| ELASTOMERS |
拉伸应力2(300%应变) |
|
ASTMD412 |
11.7 |
MPa |
| ELASTOMERS |
拉伸应力2(300%应变) |
|
DIN53504 |
11.7 |
MPa |
| ELASTOMERS |
抗张强度2(断裂) |
|
ASTMD412 |
28.3 |
MPa |
| ELASTOMERS |
拉伸应力2(断裂) |
|
DIN53504 |
35.0 |
MPa |
| ELASTOMERS |
伸长率2(断裂) |
|
ASTMD412 |
600 |
% |
| ELASTOMERS |
伸长率2(断裂) |
|
DIN53504 |
820 |
% |
| ELASTOMERS |
撕裂强度2 |
|
ASTMD624 |
99.8 |
kN/m |
| ELASTOMERS |
撕裂强度2 |
|
ISO34-1 |
80 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ASTMD395 |
30 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
42 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ISO815 |
30 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ISO815 |
42 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ASTMD2240 |
85 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ASTMD2240 |
36 |
|
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
DIN53505 |
85 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
DIN53505 |
36 |
|
| 热性能 |
TMA3 |
High:635.0µm |
InternalMethod |
160 |
°C |
| 热性能 |
TMA3 |
Low:635.0µm |
InternalMethod |
116 |
°C |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
CalendarTemperatureProfile4 |
FrontRoll |
|
160to180 |
°C |
| ADDITIONAL INFORMATION |
CalendarTemperatureProfile4 |
RearRoll |
|
160to180 |
°C |