| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.16 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53479 |
1.16 |
g/cm³ |
| 物理性能 |
溶化体积流率（MVR）(190°C/5.0kg) |
|
|
30.0 |
cm³/10min |
| 物理性能 |
收缩率-流动(注塑) |
|
ASTMD955 |
0.90 |
% |
| 机械性能 |
Abrasion2 |
|
DIN53516 |
30 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
DIN53504 |
3.40 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
DIN53504 |
7.00 |
MPa |
| ELASTOMERS |
TensileStress3(Break,0.635mm) |
|
DIN53504 |
45.0 |
MPa |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
DIN53504 |
770 |
% |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
DIN53515 |
45 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ASTMD395 |
34 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
48 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
DIN53517 |
34 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
DIN53517 |
48 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ASTMD2240 |
68 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ASTMD2240 |
20 |
|
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
DIN53505 |
68 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
DIN53505 |
21 |
|
| 热性能 |
TMA3 |
High:635.0µm |
InternalMethod |
165 |
°C |
| 热性能 |
TMA3 |
Low:635.0µm |
InternalMethod |
120 |
°C |