| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.16 |
g/cm³ |
| 机械性能 |
TensileModulus(2.20mm,InjectionMolded) |
|
ASTMD412 |
152 |
MPa |
| 机械性能 |
FlexuralModulus(2.20mm,InjectionMolded) |
|
ASTMD790 |
165 |
MPa |
| 机械性能 |
泰伯耐磨性 |
|
ASTMD1044 |
60.0 |
mg |
| 机械性能 |
Abrasion-DIN |
|
DIN53516 |
30 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress(100%Strain,2.20mm) |
|
ASTMD412 |
26.2 |
MPa |
| ELASTOMERS |
TensileStress(300%Strain,2.20mm) |
|
ASTMD412 |
45.5 |
MPa |
| ELASTOMERS |
TensileStrength(2.20mm) |
|
ASTMD412 |
48.3 |
MPa |
| ELASTOMERS |
TensileElongation(Break,2.20mm) |
|
ASTMD412 |
410 |
% |
| ELASTOMERS |
TearStrength2(2.20mm) |
|
ASTMD624 |
210 |
kN/m |
| ELASTOMERS |
压缩永久变形 |
23°C,22hr |
ASTMD395B |
40 |
% |
| ELASTOMERS |
压缩永久变形 |
70°C,22hr |
ASTMD395B |
50 |
% |
| 硬度 |
肖氏硬度(邵氏D) |
|
ASTMD2240 |
54 |
|
| 热性能 |
玻璃转化温度 |
|
InternalMethod |
-16.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
138 |
°C |
| 热性能 |
SofteningPoint-DMA |
|
InternalMethod |
127 |
°C |