| 规格级别 | 其它 薄膜 挤出 | 外观颜色 | |
| 该料用途 | 薄膜，吹塑成型应用，铸造薄膜 | ||
| 备注说明 | 芳香,高弹性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
|
物理性能
|
比重 | ASTM D-792 | 1.22 | g/cm³ | |
| 熔流率 | 190°C/8.7 kg | ASTM D-1238 | 14 | g/10 min | |
| 硬度计硬度 | 支撐 A, 5 秒 | ASTM D-2240 | 87 到 93 | ||
|
机械性能
|
抗泰伯磨耗 | 1000 Cycles, 1000 g, H-18 转轮 | ASTM D-3389 | 40.0 | mg |
| 拉伸永久变形 | 200% 应变 | ASTM D-412 | 18 | % | |
| 水气透过率 | 3°C, 90% RH 1 | ASTM D-6701 | 3000 | g/m²/24 hr | |
| 23°C, 50% RH 2 | ASTM E96 | 500 | g/m²/24 hr | ||
| 拉伸应力 | 100%应变 | ASTM D-412 | 6.21 | MPa | |
| 300%应变 | ASTM D-412 | 13.8 | MPa | ||
| 抗张强度 | 断裂 | ASTM D-412 | 34.5 | MPa | |
| 伸长率 | 断裂 | ASTM D-412 | 550 | % | |
| 撕裂强度 | -- 3 | ASTM D-624 | 78.8 | kN/m | |
| 开裂 | ASTM D-470 | 20 | kN/m | ||
| 压缩永久变形 | 23°C, 22.0 hr | ASTM D-395 | 17 | % | |
| 70°C, 22.0 hr | ASTM D-395 | 79 | % | ||
| 老化 | 体积变化 | 23°C, 24 hr | ASTM D-471 | 40 | % |
| 热性能 | 玻璃转化温度 | DSC | Internal Method | -23.9 | ℃ |
| 熔融温度 | Internal Method | 144 | ℃ | ||
| Internal Method | 155 | ℃ | |||