| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 机械性能 |
拉伸强度 |
|
ASTM D-412（ASTM D-638） |
37.9 |
MPa |
| 比重 |
|
ASTM D-792 |
1.20 |
|
| Brookfield Viscosity |
15% T.S.in THF |
RVT Spindle #2,20 RPM,23℃ |
800-1300 |
cps |
| Green Strength |
|
|
5.5 |
KN/m |
| 100%模量伸长率 |
|
ASTM D-412（ASTM D-638） |
4.7 |
MPa |
| 300%模量伸长率 |
|
ASTM D-412（ASTM D-638） |
9.0 |
MPa |
| 肖氏硬度 |
|
ASTM D-2240 |
40D |
|
| Final Peel Strength |
|
|
7.2 |
KN/m |
| Open Tack Time |
|
|
5 |
hours |
| 极限伸长率 |
|
ASTM D-412（ASTM D-638） |
600 |
% |
| 热性能 |
玻璃化转变温度 |
|
DSC |
-43 |
℃ |
| Heat Resistance |
|
BFG 899 |
93 |
℃ |
| Heat Activation |
|
|
54 |
℃ |
| 其它性能 |
Melt Viscosity @ 204 C(400℃) |
|
ASTM D-1084-88 |
130,000 |
cps |
| Ring and Ball Softening Point |
|
ASTM E-28-92 |
170 |
℃ |
| Gradient Bar Tack Temperature |
|
|
84 |
℃ |
| T-peel,Aluminum Foil |
|
ASTM D-1876-72 |
0.4 |
KN/m |
| T-peel,Mylar Film |
|
ASTM D-1876-72 |
5.3 |
KN/m |
| Open Time |
|
ASTM D-4497-94 |
＞315 |
sec |