| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.19 |
|
| 机械性能 |
100%模量伸长率 |
|
ASTM D-412（ASTM D-638） |
2.3 |
MPa |
| 洛氏硬度 |
|
ASTM D-2240 |
70A |
|
| Brookfield Viscosity |
15% T.S.in 80:20 MEK:TOL |
|
250 |
cps |
| Adhesion to PET |
Cast in cyclohexanone |
TP-141 |
0.12 |
KN/m |
| 极限伸长率 |
|
ASTM D-412（ASTM D-638） |
630 |
% |
| 拉伸强度 |
|
ASTM D-412（ASTM D-638） |
31.0 |
MPa |
| 300%模量伸长率 |
|
ASTM D-412（ASTM D-638） |
3.8 |
MPa |
| Brookfield Viscosity |
15% T.S.in cyclohexanone |
|
1600 |
cps |
| Adhesion to PET |
Cast in MEK |
TP-141 |
0.11 |
KN/m |
| 热性能 |
玻璃化转变温度 |
|
DSC |
-31 |
℃ |
| 其它性能 |
T-peel,Aluminum Foil |
|
ASTM D-1876-72 |
1.8 |
KN/m |
| Ring and Ball Softening Point |
|
ASTM E-28-92 |
179 |
℃ |
| Open Time |
|
ASTM D-4497-94 |
＞300 |
sec |
| Melt Viscosity @ 204 C(400℃) |
|
ASTM D-1084-88 |
92000 |
cps |
| Gradient Bar Tack Temperature |
|
|
91 |
℃ |
| T-peel,Mylar Film |
|
ASTM D-1876-72 |
3.4 |
KN/m |