| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.03 | % | |
| 物理性能 | 流动系数 | 200℃,5kg/cm2 | ASTM D-1238 | 2.5 | g/10min |
| 比重 | ASTM D-792 | 1.05 | |||
| 成型收缩率 | ASTM D-955 | 0.3-0.6 | % | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 100 | L scale | |
| 伸长率 | ASTM D-638 | 8.0 | % | ||
| 洛氏硬度 | ASTM D-785 | 80 | M scale | ||
| 弯曲弹性率 | ASTM D-790 | 30000 | kg/cm2 | ||
| 引张强度 | ASTM D-638 | 550 | kg/cm2 | ||
| IZOD冲击强度 | ASTM D-256 | 2.2 | kg.cm/cm | ||
| 引张弹性率 | ASTM D-638 | 25000 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 1000 | kg/cm2 | ||
| 电气性能 | 透电率 | ASTM D-150 | 2.5 | 106cycle/see | |
| 耐电压 | ASTM D-149 | 500 | V/mil | ||
| 体积抵抗率 | ASTM D-257 | 1016 | Ω.cm | ||
| 热性能 | 燃烧性 | UL 94 | HB | CLASS | |
| 加热变形温度 | 6.4mm 18.6kg/cm2Unannealed | ASTM D-648 | 92 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 107 | ℃ | ||
| 加热变形温度 | 6.4mm 18.6kg/cm2Annealed | ASTM D-648 | 99 | ℃ | |