| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.888 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(230°C/2.16kg) | ASTMD1238 | 3.0 | g/10min | |
| ELASTOMERS | 弹性体 | TestMethod | NominalValue | Unit | |
| ELASTOMERS | 拉伸应力2 | 横向流量:100%应变 | ASTMD412 | 7.18 | MPa |
| ELASTOMERS | 拉伸应力2 | 流量:100%应变 | ASTMD412 | 9.88 | MPa |
| ELASTOMERS | 拉伸应力2 | 横向流量:300%应变 | ASTMD412 | 7.97 | MPa |
| ELASTOMERS | 拉伸应力2 | 流量:300%应变 | ASTMD412 | 11.4 | MPa |
| ELASTOMERS | 抗张强度2 | 断裂 | ASTMD412 | 17.0 | MPa |
| ELASTOMERS | 抗张强度2 | 流量:断裂 | ASTMD412 | 14.0 | MPa |
| ELASTOMERS | 伸长率2 | 断裂 | ASTMD412 | 760 | % |
| ELASTOMERS | 伸长率2 | 流量:断裂 | ASTMD412 | 480 | % |
| ELASTOMERS | 压缩永久变形3 | 23°C,22hr | ASTMD395B | 36 | % |
| ELASTOMERS | 压缩永久变形3 | 70°C,22hr | ASTMD395B | 55 | % |
| 硬度 | 肖氏硬度 | 邵氏A,1秒,注塑 | ASTMD2240 | 94 | |
| 硬度 | 肖氏硬度 | 邵氏A,5秒,注塑 | ASTMD2240 | 92 | |