| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.15to1.19 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
抗张强度 |
0.635mm |
ASTMD412 |
13.8 |
MPa |
| ELASTOMERS |
抗张强度 |
1.91mm |
ASTMD412 |
12.4 |
MPa |
| ELASTOMERS |
伸长率 |
Break,1.91mm |
ASTMD412 |
340 |
% |
| ELASTOMERS |
伸长率 |
Break,0.635mm |
ASTMD412 |
300 |
% |
| 硬度 |
肖氏硬度 |
邵氏A |
ASTMD2240 |
71to77 |
|
| 硬度 |
肖氏硬度 |
邵氏A,15秒 |
ASTMD2240 |
62to68 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-53.0 |
°C |
| 热性能 |
Deformation-retention,1hour(150°C,635.0µm) |
|
|
65 |
% |
| 老化 |
ChangeinTensileStrengthinAir2(136°C,168hr) |
|
ULUnspecified |
30 |
% |
| 老化 |
空气中极限伸长率的变化率2(136°C,168hr) |
|
ULUnspecified |
-25 |
% |
| 可燃性 |
极限氧指数(3.18mm) |
|
ASTMD2863 |
24 |
% |