| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.938 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(200°C/5.0kg) |
|
ASTMD1238 |
1.3 |
g/10min |
| 物理性能 |
溶液粘度 |
|
ASTMD2196 |
300 |
mPa·s |
| 物理性能 |
StyreneContent |
|
内部方法 |
30.0 |
wt% |
| 物理性能 |
灰份含量 |
|
ASTMD1416 |
0.2 |
wt% |
| 硬度 |
肖氏硬度(邵氏A,1秒) |
|
ASTMD2240 |
62 |
|
| 弹性体 |
拉伸应力1(300%应变,25°C) |
|
ASTMD412 |
4.21 |
MPa |
| 弹性体 |
抗张强度2(屈服,25°C) |
|
ASTMD412 |
26.2 |
MPa |
| 弹性体 |
伸长率3(断裂,-4°C) |
|
ASTMD412 |
900 |
% |
| 弹性体 |
应力松弛4 |
[email protected]%strainA:23°C,889.0µm |
|
1.52 |
MPa |
| 弹性体 |
应力松弛4 |
[email protected]%strain:23°C,889.0µm |
|
5.45 |
MPa |
| 弹性体 |
应力松弛4 |
RatioA:B:23°C,889.0µm |
|
2.50 |
|
| 弹性体 |
应力松弛4 |
[email protected]%strain:23°C,889.0µm |
|
7.2 |
% |
| 弹性体 |
应力松弛4 |
Setafter500%strain:23°C,889.0µm |
|
13 |
% |
| 弹性体 |
应力松弛4 |
[email protected]%strain:23°C,889.0µm |
|
0.483 |
MPa |
| 弹性体 |
应力松弛4 |
[email protected]%strainB:23°C,889.0µm |
|
0.621 |
MPa |
| 补充信息 |
DiblockContent |
|
|
|
wt% |
| 补充信息 |
挥发性 |
|
内部方法 |
0.2 |
wt% |