| 规格级别 | 清晰度，高,良好的柔韧性,食品接触的合规性,韧性良好,共聚物 注射成型,吹塑成型,薄膜挤出 | 外观颜色 | |
| 该料用途 | 层压板,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.50 | g/10min | |
| 物理性能 | 醋酸乙烯含量 | 13.5 | wt% | ||
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm,吹塑薄膜 | ASTMD882 | 90.3 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm,吹塑薄膜 | ASTMD882 | 91.0 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 6.62 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 5.52 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 30.5 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 29.8 | MPa |
| 薄膜 | 伸长率 | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 18 | % |
| 薄膜 | 伸长率 | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 16 | % |
| 薄膜 | 伸长率 | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 300 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 600 | % |
| 薄膜 | 落锤冲击(38µm,吹塑薄膜) | ASTMD4272 | 570 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm,吹塑薄膜 | ASTMD1922 | 92 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm,吹塑薄膜 | ASTMD1922 | 130 | g |
| 薄膜 | 氧气传输速率(23°C,38µm,吹塑薄膜) | ASTMD3985 | 8900 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(38°C,38µm,吹塑薄膜) | ASTMF372 | 85 | g/m²/24hr | |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm,吹塑薄膜 | ASTMD882 | 90.3 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm,吹塑薄膜 | ASTMD882 | 91.0 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 6.62 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 5.52 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 30.5 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 29.8 | MPa |
| 薄膜 | 伸长率 | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 18 | % |
| 薄膜 | 伸长率 | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 16 | % |
| 薄膜 | 伸长率 | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 300 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 600 | % |
| 薄膜 | 落锤冲击(38µm,吹塑薄膜) | ASTMD4272 | 570 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm,吹塑薄膜 | ASTMD1922 | 92 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm,吹塑薄膜 | ASTMD1922 | 130 | g |
| 薄膜 | 氧气传输速率(23°C,38µm,吹塑薄膜) | ASTMD3985 | 8900 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(38°C,38µm,吹塑薄膜) | ASTMF372 | 85 | g/m²/24hr | |
| 热性能 | 脆化温度 | ASTMD746 | <-76.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 80.0 | °C | |
| 热性能 | 熔融温度 | DSC | 94.4 | °C | |
| 光学性能 | 光泽度(45°,38.1µm,吹塑薄膜) | ASTMD2457 | 88 | ||
| 光学性能 | 雾度(38.1µm,吹塑薄膜) | ASTMD1003 | 1.5 | % | |
| 补充信息 | NAS2(38.1µm) | ASTMD1746 | 78.0 | ||