| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.45 | g/10min | |
| 物理性能 | 醋酸乙烯含量 | 12.5 | wt% | ||
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 80.7 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 88.9 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm | ASTMD882 | 11.3 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm | ASTMD882 | 5.58 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 38.7 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 32.2 | MPa |
| 薄膜 | 伸长率 | MD:屈服,38µm | ASTMD882 | 59 | % |
| 薄膜 | 伸长率 | TD:屈服,38µm | ASTMD882 | 10 | % |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 470 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 650 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm | ASTMD1922 | 56 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm | ASTMD1922 | 150 | g |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 80.7 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 88.9 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm | ASTMD882 | 11.3 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm | ASTMD882 | 5.58 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 38.7 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 32.2 | MPa |
| 薄膜 | 伸长率 | MD:屈服,38µm | ASTMD882 | 59 | % |
| 薄膜 | 伸长率 | TD:屈服,38µm | ASTMD882 | 10 | % |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 470 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 650 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm | ASTMD1922 | 56 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm | ASTMD1922 | 150 | g |
| 热性能 | 脆化温度 | ASTMD746 | -76.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 80.0 | °C | |
| 热性能 | 熔融温度 | DSC | 96.4 | °C | |
| 光学性能 | 光泽度(45°,38.1µm) | ASTMD2457 | 85 | ||
| 光学性能 | 透明度(38.1µm) | ASTMD1746 | 82.0 | ||
| 光学性能 | 雾度(38.1µm) | ASTMD1003 | 1.2 | % | |