EVA | UE631
生产厂家：台湾聚合
规格用途
| 规格级别 |
其它 发泡 其它 |
外观颜色 |
|
| 该料用途 |
鞋底发泡挤压，薄膜挤压 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 其它性能 |
薄膜 |
MD |
|
ASTM D-638/D-882 |
480 |
% |
| TD |
|
ASTM D-638/D-882 |
640 |
% |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.942 |
g/cm3 |
| 机械性能 |
冲击强度 |
|
ASTM D-1709 |
374 |
G/F50 |
| 其它性能 |
铸膜成型 |
|
ASTM D-638/D-882 |
180 |
kg/cm2 |
| 硬度 |
|
ASTM D-2240 |
36 |
Shore D |
| 低温易脆性 |
|
ASTM D-746 |
<-76 |
℃/F50 |
| 射出 |
|
ASTM D-638/D-882 |
250 |
% |
| VA含量 |
|
ASTM USIFE |
22 |
% |
| 薄膜 |
MD |
|
ASTM D-638/D-882 |
264 |
kg/cm2 |
| TD |
|
ASTM D-638/D-882 |
189 |
kg/cm2 |
| 熔融指数 |
|
ASTM D-1238 |
1.4 |
g/10min |
| VICAT 软化点 |
|
ASTM D-1525 |
64 |
℃ |
| 融化点 |
|
ASTM D-2117 |
82 |
℃ |
| 射出 |
|
ASTM D-638/D-882 |
110 |
kg/cm2 |
| 铸膜成型 |
|
ASTM D-638/D-882 |
800 |
% |
-
-