| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.951 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO1183 |
0.951 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
150to210 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ISO1133 |
150to210 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
26.0to30.0 |
wt% |
| 物理性能 |
MaleicAnhydrideContent |
|
|
6400 |
ppm |
| 机械性能 |
TensileStrength2(Break,2.80mm,CompressionMolded) |
|
ASTMD638 |
5.50 |
MPa |
| 机械性能 |
TensileStress(Break,2.80mm,CompressionMolded) |
|
ISO527-2/5A/50 |
5.50 |
MPa |
| 机械性能 |
TensileElongation2(Break,2.80mm,CompressionMolded) |
|
ASTMD638 |
700to900 |
% |
| 机械性能 |
TensileStrain(Break,2.80mm,CompressionMolded) |
|
ISO527-2/5A/50 |
700to900 |
% |
| 硬度 |
DurometerHardness(ShoreA,15sec,2.80mm,CompressionMolded) |
|
ASTMD2240 |
75 |
|
| 硬度 |
ShoreHardness(ShoreA,15sec,2.80mm,CompressionMolded) |
|
ISO868 |
75 |
|
| 热性能 |
维卡软化温度 |
|
ASTMD15253 |
<40.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ISO306/A |
<40.0 |
°C |
| 热性能 |
熔融温度 |
|
ISO11357-3 |
68.0 |
°C |
| 热性能 |
RingandBallSofteningPoint |
|
ASTME28 |
92 |
°C |