| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
11 |
g/10min |
| 物理性能 |
抗环境应力开裂 |
10%Igepal,RotationalMolded,F50 |
ASTMD1693A |
1.00 |
hr |
| 物理性能 |
抗环境应力开裂 |
100%Igepal,RotationalMolded,F50 |
ASTMD1693A |
4.00 |
hr |
| 物理性能 |
抗环境应力开裂 |
醋酸乙烯含量 |
ASTMD1693A |
9.0 |
wt% |
| 机械性能 |
TensileStrength2(Yield,3.18mm,RotationalMolded) |
|
ASTMD638 |
11.7 |
MPa |
| 机械性能 |
FlexuralModulus-1%Secant(3.18mm,RotationalMolded) |
|
ASTMD790 |
95.1 |
MPa |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,滚塑成形) |
|
ASTMD648 |
37.0 |
°C |
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,RotationalMolded) |
|
ASTMD648 |
23.0 |
°C |