| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 2.3 |
g/10 min
|
| 醋酸乙烯含量 | ExxonMobil Method | 26.2 |
wt%
|
||
| 机械性能 |
割线模量 |
1% 正割, MD
|
ASTM D882 | 29.2 |
MPa
|
| |
1% 正割, TD
|
ASTM D882 | 31.4 |
MPa
|
|
| 抗张强度 |
MD: 断裂
|
ASTM D882 | 35.1 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 34.7 |
MPa
|
||
| 伸长率 | MD: 断裂 | ASTM D882 | 450 | % | |
|
TD: 断裂
|
ASTM D882 | 730 | % | ||
| 落锤冲击 | ASTM D1709A | 460 | g | ||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 38 | g | |
|
TD
|
ASTM D1922 | 460 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 48.0 |
°C
|
|