| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.930 |
g/cm³
|
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 2.0 |
g/10 min
|
|
| 醋酸乙烯含量 | ExxonMobil Method | 8.7 |
wt%
|
||
| 机械性能 | 割线模量 | 1% 正割, MD | ASTM D882 | 108 |
MPa
|
|
1% 正割, TD
|
ASTM D882 | 120 |
MPa
|
||
| 抗张强度 |
MD: 断裂
|
ASTM D882 | 30.5 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 27.4 |
MPa
|
||
| 伸长率 |
MD: 断裂
|
ASTM D882 | 330 |
%
|
|
|
TD: 断裂
|
ASTM D882 | 660 |
%
|
||
| 落锤冲击 | ASTM D1709A | 250 | g | ||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 120 | g | |
|
TD
|
ASTM D1922 | 95 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 81.0 |
°C
|
|