| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率 | ASTM D1238 | 2.1 | g/10 min | |
| 醋酸乙烯含量 | 190°C/2.16 kg) | ExxonMobil Method | 9.4 |
wt%
|
|
| 支撐硬度 | 支撐 A, 15 秒 | ISO 868 | 93 | ||
| 机械性能 | 拉伸模量 | ISO 527-2 | 90.0 |
MPa
|
|
| 割线模量 |
1% 正割, MD
|
ASTM D882 | 90.0 |
MPa
|
|
|
1% 正割, TD
|
ASTM D882 | 95.0 |
MPa
|
||
| 抗张强度 |
MD: 断裂
|
ASTM D882 | 28.0 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 27.0 |
MPa
|
||
| 伸长率 |
MD: 断裂
|
ASTM D882 | 550 |
%
|
|
|
TD: 断裂
|
ASTM D882 | 650 |
%
|
||
| 落锤冲击 | ASTM D1709A | 390 | g | ||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 120 | g | |
|
TD
|
ASTM D1922 | 190 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 78.5 |
°C
|
|